PLIBRICO CASTABLE REFRACTORIES & PLASTIC MATERIAL

MATERIALS
CASTABLE REFRACTORIES
PLASTIC MATERIALS
TYPE
Plicast
27
Plicast
31. R
Plibrico
Super AB
Plibrico
Superal. XAB
Maximum Service
Temperatur (0°C)
1320
1500
1540
1650
Permanent Linear
Change [%] After
Firing at    110°C
              1100°C
              1300°C 


-0,05
-0,30
    -


-0,10
-0,15
-1,00


-1,45
-1,75
-1,55


-1,30
-1,45
-0,50
Bulk Density after
Firing at 1100°C
1,93
2,04
2,06
2,42
Cold Comprressive
Strength [N/mm²]
After Firing at    110°C
                       1100°C
                       1300°C



20
11
-



23
18
33



6,0
15
17



6,0
17
12
Reversible Thermal
Expansion at 1000°C
0,60
0,55
0,63
0,70
Thermal
Conductivity
(Tm=1100°C)
(W/mK)
0,78
0,92
1,21
1,31
Chemical Analysis
AL2 O3 (%)
Si O2     (%)
Fe2 O3  (%)
CaO      (%)

35
49
3,2
9,0

46
42
1,5
7,0

40
55
1,2
-

70
23
1,2
Materials Required
(Ton/M³)
1,95
2,05
2,25
2,62
Water Addition on
Site (%)
13, 5-14,5
10-11
-
-
Net Weight per bag
(Kg)
25
25
25
25

Back

SUPER CASTABLE REFRACTORIES

MATERIALS
SUPER CASTABLE REFRACTORIES
TYPE
SCD. 13
SCR. 14
SCR. 15
SCR. 16
Maximum Service
Temperature (0°C)
1300
1400
1500
1650
Permanent Linear
Change After Heat
ting for 3 hours at
the Temperatures in parenheses


0,2
(1300)


0,2
(1400)


0,3
(1500)


0,5
(1650)
Bulk Density after
Firing at 1100°C
1,9
2,00
2,10
2,70
Cold Comprrehenssive
Streng [Kg/Cm²]
After Firing at
                     110°C
                   1100°C
                   1300°C



40
40
-



45
30
70



30
25
80



50
35
60
Reversible Thermal
Expansion at 1000°C
0,60
0,55
0,63
0,70
Thermal
Conductivity
(Tm=1100°C)
(W/mK)
0,72
0,88
1,61
1,40
Chemical Analysis
AL2 O3 (%)
Si O2     (%)
Fe2 O3  (%)
CaO      (%)

42
46
3,1
9,0

47
43
1,3
7,0

52
42
1,1
-

64
30
0,8
Materials Required
(Ton/M³)
1,90
2,00
2,10
2,22
Water Addition on
Site (%)
13
14
12
10-11
Net Weight per bag
(Kg)
25
25
25
25

Back

 

FIRE CLAY BRICK & HIGH ALUMINA BRICK

PRODUCTS
FIRE CLAY BRICK
HIGH ALUMINA BRICK
TYPE
T. F B
T. H B
HA-3
HA-2
HA-1
Maximum Service
Temperature (0°C)
1.550
1.600
1.650
1.750
1.800
Bulk Density G/Cm³
2,5
2,7
3,1
3,3
3,8
Thermal Conductivity at
1000°C (Kcal/m hr°C)
<1,6
<1,5
<1,4
<1,6
<1,3
Thermal Linear Expansion
at 1000°C (%)
0,5
0,6
0-0,4
0-0,5
0-0,6
Permanen Linear Change
on Reheating at 1500°C
for 2 hrs (%)
0,2
0,5
0,5-1
0,3
0,5
Chemical Composition   %
               AL2  O3
                  Si   O2
               Fe2   O3

36-40
55
2,5

40-48
40
1,8

55
22
1,5

65
15
1,3

70
10
1,1

Back

 REFRACTORIES MORTAR

PRODUCT TYPE STA.SK.32 STA.SK.34 STA.SK.34 STA.SK.38
Suhu Kerja Maximum
Dalam (0°C)
1.200 1.400 1.600 1.700
Komposisi Kimia
     A12 O3 (%)
       Si  O2 (%)
     Fe2 O3 (%)

35
57
2,3

45
50
1,8

57
32
1,2

70
19
0,7
Ukuran Butir (%)
   + 0,5 mm
   - 0,74 mm

<2
<35

<2
<37

<2
<40

<2
<40
Pemakaian Fire Clay Brick High Alumina Brick

Back

 

INSULATING FIREBRICK

PRODUCTS/PROPERTIES
INSULATING FIREBRICK
TYPE
B. 1
B. 2
C. 1
C. 2
C. 3
Maximum Service
Temperature (0°C)
900
1000
1300
1400
1500
Bulk Density G/Cm³
0,65
0,70
1,06
1,14
1,23
Thermal Conductivity
K Cal/mh C at 300°C
Mean

0,15

0,17

0,28

0,32

0,42
Rehead shrinkage
% at ( ) C x 8 hrs
0,68
900
0,78
1000
0,57
1300
0,59
1400
0,41
1500
Cold Srushing
Strength Kg/Cm²
33
33
63
78
119
Modulus of Rupture
Kg/Cm
15
18
25
32
49
Thermal Expansion
% at ( ) °C
0,10
900
0,23
1000
0,51
1000
0,49
1000
0,46
1000
Chemical Composition   %
               AL2  O3
                  Si   O2
               Fe2   O3

12
78
4,2

12
79
3,6

30
65
1,8

35
61
1,6

59
38
1,2
Raw Material
Fire Clay